DOWSIL 813C Construction and concrete silicone

Name: DOWSIL 813C Construction and concrete silicone
Brand: Dow
Price: 48.43 PLN
Availability: OutOfStock

71,40 zl PLN Save -71,40 zl PLN

Tax includedShipping calculated at checkout

Only 48 left!

Color: Black (Black)

Capacity: 600ml (sausage)

Cechy szczególne: Dobra przyczepność do wielu podłoży, Dobra wodoodporność, Klej/uszczelniacz jednoskładnikowy, Utwardzanie Alkoxy (Neutralny))

Niska temperatura: od -31°C do -50°C

Pojemność opakowania: 310ml

Typ produktu: Silikon

Wysoka temperatura: +131°C do 150°C

Zastosowanie: Szklenie strukturalne i uszczelnianie fasad

DOWSIL™ 813C Construction & Concrete Silicone

What is Dowsil 813 construction and concrete silicone?

One-component, neutral-curing construction silicone for porous surfaces.

A low modulus silicone sealant, particularly suitable for interior and exterior applications, in particular exterior weather seals, expansion joints, perimeter joints in buildings and other types of construction.

Application:

Indoor and outdoor applications
External weather seals
Expansion joints and circumferential joints in buildings and other structures,
Joints in footpaths and communication routes
Sealing of sidewalks and roads in places that are not exposed to fuel flooding

Features and Benefits:

Adhesion to Brick, Concrete, Glass, Masonry, Metal, Polyester Powder coated Aluminium/Steel, Vinyl/PVC-U, Wood
Excellent weather resistance - virtually insensitive to sunlight, rain, snow, ozone and extremes
tensile/compressive joint displacement capacity ± 50% of joint width
Temperature resistance from -40°C to 149°C
Good adhesion without priming to various substrates
Resistant to ozone, ultraviolet radiation and extreme temperatures
Neutral curing with titanium (Ti) catalyst
low odor, easy to apply and process
compliant with PN-EN ISO 11600-F&G-20LM

Basic parameters and properties of Dowsil 813C silicone

Test	Property	Unit	Value
	Binding system		Alkoxy (neutral)
	Application temperature, application	°C	+5 to +50
	Temperature resistance	°C	-40 +149
CTM1 97B	Density		1.51
CTM 364C	Juicing speed	g/minute	240
CTM 98B	Skin formation time (23°C, 50% RH)	minutes	20
CTM 95A	Time to dust dry (23°C, 50% RH)	minutes	thirty
CTM 663A	Setting time (23°C, 50% RH) 1 Day
CTM 663A	Setting time (23°C, 50% RH) 1 Day	mm	2
	Three days	mm	4
	Joint 2 mm thick S2 dumb-bells (ISO2 37/DIN3 53 504)
CTM 137 A	Modulus at 100% elongation	MPa	0.45
CTM 137 A	Tensile strength	MPa	1.9
CTM 137 A	Elongation at break	%	700
Technically approved joint 12x12x50 mm structural joint TA (ISO 8339/DIN 2-8339)
CTM 677	Modulus at 100% elongation	MPa	0.35
CTM 677	Tensile strength	MPa	0.75
CTM 677	Elongation at break	%	380
CTM 99E	Hardness measured with a hardness tester	Shore A	29
ISO 7389	Post-deformation recovery	%	> 90
ISO 9047	Movement ability	%	±50

Specifications and Standards

Complies with SNJF standard (F&G - 25E)
ISO 11600-F-25LM
DIN 18540 Class F
EN 15651-4
EN 14188-2 Class A

Benefits of the application

Primerless Adhesion: Primerless
Ozone resistance, heat resistance, UV resistance

Curing system One-piece neutral curing

Durability and Storage

DOWSIL™ 813C Construction and Concrete Silicone Sealant should be stored in a dry and cool place.
DOWSIL™ 813C Construction and Concrete Silicone Sealant stored at or below 30°C in the original unopened container has a shelf life of 12 months from the date of manufacture.

Packaging and Colors

DOWSIL™ 813C Construction & Concrete Silicone is supplied in 310 ml cartridges and "sausages" 600 ml

Color

Anthracite, Black , Brown, Desert Rose, Grey , Pink Coral, Red Beige, Sand, Stone, White

How to use

Substrate preparation

The surfaces to be sealed should be clean, dry, stable and degreased. Before applying the sealant, clean non-porous surfaces with DOWSIL™ R-40 Universal Cleaner and dry thoroughly with a clean, lint-free cloth. Porous materials such as concrete, brick, mortar, etc. should be mechanically cleaned of loose particles using a wire brush, grinding wheel or similar methods.

Masking. Securing

Masking tape should be used in areas adjacent to joints to protect materials from contamination and to ensure a straight seal contour. The masking tape must be removed immediately after the joint is finished.

Underlay

Primers are not usually required, but may be recommended on certain surfaces for the best adhesion.

Finish Curing time

The applied sealant should be machined within 5 minutes of application to ensure good contact between sealant and material. The joint treatment also gives it a smooth, professional look.

Cleaning

Uncured excess sealant can be removed from tools and non-porous surfaces with DOWSIL™ R-40 Universal Cleaner. If the sealant is improperly applied to a porous material, allow it to cure, then remove it by peeling, cutting, or other mechanical means. Avoid damaging plastic or coated surfaces.

Connector design

The width of the sealing joint should take into account the possibility of movement of the sealant. When forming a joint with DOWSIL™ 813C Construction and Concrete Silicone Sealant, the minimum width should be 6 mm. For joints 6-12 mm wide, the required sealing depth is 6 mm. For joints with a width of more than 12 mm, it is recommended to maintain a 2:1 ratio between width and depth. If a fillet joint is required, it is recommended that a minimum of 6mm of sealant be applied to each surface. For connectors wider than 25mm or deeper than 15mm, please contact your local technical office.